Hot Melt Adhesive for Woodworking Edge Banding – Fast Bonding, Durable Finish

Edge banding not only enhances the aesthetic appeal of products but also effectively seals harmful substances within the boards, playing an environmentally friendly role.

•Applicable Edge-banding Substrates: Particleboard, medium-density fiberboard, solid wood.

•Applicable Edge-banding Materials: PVC edge-banding, wood veneer, and melamine-based edge-banding.

Advantages:

Low Viscosity: Excellent fluidity, glue-saving, and suitable for automated lines. In molten state, it has strong fluidity and can be evenly applied. It uses less glue than high-viscosity alternatives while achieving the same bonding effect.

Fast Curing Speed: Improves bonding efficiency and adapts to mass production. After application, the hot melt glue achieves initial fixation in seconds, avoiding edge banding displacement or peeling caused by slow curing.

Good Leveling Property: Spreads quickly and evenly after application, without shrinkage cavities, glue accumulation or glue breakage, suitable for straight/irregular edge banding without manual correction; the glue layer is smooth and continuous without bubbles before curing, leveling accurately only in the bonding area without glue overflow or stringing; after curing, the glue layer has a consistent thickness, no glue lines or steps, firm bonding, and resistance to temperature changes and cracking.

Long Open Time: High operational fault tolerance, suitable for complex processes. After gluing, there is ample time to adjust the position of the edge banding strip and correct fitting deviations without rushing for curing; especially suitable for irregular edge banding, manual edge banding, or material change scenarios on assembly lines, avoiding bonding misalignment or peeling caused by rapid curing, and ensuring edge banding accuracy and bonding quality.

High Bonding Strength: Stable connection without detachment, impact resistance, and aging resistance. After curing, the hot melt glue forms a high-strength bond with the edge banding and substrates; during peeling, the filter medium breaks while the glue layer remains intact.

Good Initial Tack: Instant fixation, reducing auxiliary operations. It generates tack immediately after application, avoiding interface detachment due to poor initial tack.

Good Thread-Breaking Performance: Optimizes operational experience and avoids contamination. When pausing or switching substrates during edge banding, the hot melt glue rarely leaves residual stringing. No excess glue threads wrap around equipment or adhere to product surfaces, preventing product contamination or appearance damage.

High Cohesive Strength: Ensures transportation durability, impact resistance, and aging resistance. The cured glue layer has high inherent strength, resisting failure from external stretching or environmental changes. It can withstand impact force from extrusion and jolting, avoiding glue layer rupture and peeling.

Paint Resistance: Resistant to coating erosion, suitable for subsequent painting processes. After curing, the glue layer does not chemically react with paint or coatings, and will not swell, soften or peel off during painting (spraying or brushing).

 

 

Working Temperature: 150-210℃

Viscosity(160℃): 2000-150000

Softening point: 85-110℃

Colour: light yellow granule, white granule